Phrozen Engineering Ultra-High Temp TR300 Resin
TR300 Ultra-High Temp3D Printing Resin - Perfect for Creating 3D Printed Parts for Engineering
Phrozen TR300 3D Printing Resin comes with extremely high thermal resistance, high mechanical strength, and a certain stiffness, making it ideal for high-temperature applications such as industrial mock-ups, and creating 3D printed jewelry.
Benefits
-
ćUltra-High Temp Resistanceć With its heat deflection temperature of 160 Ā°C, Phrozen TR3003D Printing High Temp resin is suitable for high-temperature resistance applications.
-
ćLow Viscosity & Low Odorć Phrozen TR300 High Temperature 3D Printing resin has low viscosity to use and clean easily. Odorless to affect the environment during printing.
-
ćHigh Toughness & Low Shrinkageć The products printed with Phrozen TR300 High-Temp 3D Printer resin have good mechanical properties such as high tensile strength, high toughness, and a low shrinkage rate. It is recommended for industrial prototyping.
Resources
- Safety Data Sheet - Download here
- Resin Profile (Click here)
Specs
- Weight: 1kg per bottle
- Density: 1.17 g/cm3
- Viscosity: 123.6 cP
- Surface Hardness: 80 Shore D
- Tensile Stress at Break: 59.9 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 3443.7 MPa
- Notched Izod Impact: 22.1 J/m
- HDT at 0.45 MPa: 160Ā°C (w200 Ā°C, 1HR)
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Phrozen Engineering Ultra-High Temp TR300 Resin
Phrozen Engineering Ultra-High Temp TR300 Resin
TR300 Ultra-High Temp3D Printing Resin - Perfect for Creating 3D Printed Parts for Engineering
Phrozen TR300 3D Printing Resin comes with extremely high thermal resistance, high mechanical strength, and a certain stiffness, making it ideal for high-temperature applications such as industrial mock-ups, and creating 3D printed jewelry.
Benefits
-
ćUltra-High Temp Resistanceć With its heat deflection temperature of 160 Ā°C, Phrozen TR3003D Printing High Temp resin is suitable for high-temperature resistance applications.
-
ćLow Viscosity & Low Odorć Phrozen TR300 High Temperature 3D Printing resin has low viscosity to use and clean easily. Odorless to affect the environment during printing.
-
ćHigh Toughness & Low Shrinkageć The products printed with Phrozen TR300 High-Temp 3D Printer resin have good mechanical properties such as high tensile strength, high toughness, and a low shrinkage rate. It is recommended for industrial prototyping.
Resources
- Safety Data Sheet - Download here
- Resin Profile (Click here)
Specs
- Weight: 1kg per bottle
- Density: 1.17 g/cm3
- Viscosity: 123.6 cP
- Surface Hardness: 80 Shore D
- Tensile Stress at Break: 59.9 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 3443.7 MPa
- Notched Izod Impact: 22.1 J/m
- HDT at 0.45 MPa: 160Ā°C (w200 Ā°C, 1HR)
Original: $54.00
-70%$54.00
$16.20Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
TR300 Ultra-High Temp3D Printing Resin - Perfect for Creating 3D Printed Parts for Engineering
Phrozen TR300 3D Printing Resin comes with extremely high thermal resistance, high mechanical strength, and a certain stiffness, making it ideal for high-temperature applications such as industrial mock-ups, and creating 3D printed jewelry.
Benefits
-
ćUltra-High Temp Resistanceć With its heat deflection temperature of 160 Ā°C, Phrozen TR3003D Printing High Temp resin is suitable for high-temperature resistance applications.
-
ćLow Viscosity & Low Odorć Phrozen TR300 High Temperature 3D Printing resin has low viscosity to use and clean easily. Odorless to affect the environment during printing.
-
ćHigh Toughness & Low Shrinkageć The products printed with Phrozen TR300 High-Temp 3D Printer resin have good mechanical properties such as high tensile strength, high toughness, and a low shrinkage rate. It is recommended for industrial prototyping.
Resources
- Safety Data Sheet - Download here
- Resin Profile (Click here)
Specs
- Weight: 1kg per bottle
- Density: 1.17 g/cm3
- Viscosity: 123.6 cP
- Surface Hardness: 80 Shore D
- Tensile Stress at Break: 59.9 MPa
- Elongation at Break: 3.9 %
- Tensile Modulus: 3443.7 MPa
- Notched Izod Impact: 22.1 J/m
- HDT at 0.45 MPa: 160Ā°C (w200 Ā°C, 1HR)